105WCr6 | 1.2419 Tool Steel China suppliers, wholesale,  distributors, and stockholders. W-Nr. 1.2419 is equivalent to 105WCr6. Otai Special Steel is manufacturers and Has large quantity Stock in the warehouse.  We supply in Round bar, gauge plate steel, pipe / Tube, rod, square, hexagonal, blanks, plate, sheet, precision ground flat bar, precision ground bar stock, and hollow bar. provide black surface and black surface alloy steel material.

105WCr6 | 1.2419 is a German Cold work tool alloy steel material grade.it is shock resisting steel. it belongs to DIN 17350 standard. Digital Grade material number W-Nr 105WCr6 | 1.2419, Metal Steel grade X210CrW12.  It is a die steel, use in extrusion molds, Hot Cast molds. like aluminum production, Aluminium cast mold. Our Tool Steel material 100 % ultrasonic tested at good price. Small size steel products make by hot rolled, large size steel products make by forging. 1.2419 tool steel with 105WCr6 is equivalent Belong to W-Nr and DIN.

1.2419 steel round bar

Applications of 105WCr6 | 1.2419 Steel
Cutting and punching tools for sheet thickness up to 6 mm, also for paper and plastics, roll shear blades for sheet thickness up to 6 mm, small bending and drawing tools, thread cutting tools, reamers, woodworking tools, gauges and other measuring tools, small inserts, and plastic molds. 

105WCr6 | 1.2419 Steel material properties datenblatt as below:

Chemical composition data of Metal 105WCr6 | 1.2419 Cold work tool steel-DIN 17350-1980 (EN4957-2001)

C Si Mn P S W Cr
1.00～1.10 0.10～0.40 0.80～1.10 0.03 max 0.03 max 1.00～1.30 0.90～1.10

The material equivalent of DIN 105WCr6 | 1.2419 tool steel

USA Germany China Japan France England Italy Poland Czechia Austria Sweden Spain
– DIN,WNr GB JIS AFNOR BS UNI PN CSN ONORM SS UNE
L3 105WCr6 | 1.2419 SKS31 105WC13 10WCr6 2140 105WCr5

Physical properties of 105WCr6 | 1.2419 Tool Steel

  • Density: 7.85kg/m3
  • Thermal conductivity:
  • Forging ratio: 4:1 Minimum
  • Microstructure:
  • Magnetic:

Mechanical properties of Alloy Steel 105WCr6 | 1.2419 tool steel

  • Hardness： Annealling  230 HB max, Q+T: 54-64 HRC, different hardness according different Tempering temperature.
  • Yield strength:

105WCr6 | 1.2419 tool steel Heat treatment:

  • Annealing: Annealing temperature/℃: 720~750; After the annealing, degree of hardness ≤HBS: 230
  • Quenching: Hardening temperature/℃: 800~830, Quenching in Oil
  • Tempering: Commonly used drawing temperature/℃: 150~250;  After tempering hardness HRC | 100 ℃ : 64; After tempering hardness HRC | 200 ℃ : 61; After tempering hardness HRC | 300 ℃ : 58 ; After tempering hardness HRC | 400 ℃ : 54
  • Normalizing：at Normalizing temperature, then cool in furnace

 

Forged steel properties of Cold work tool 105WCr6 | 1.2419 tool steel

For forging 105WCr6 | 1.2419 steel, Slowly Pre-heat, at Hot-working temperature/℃: 1050~850

Processing of Steel Material 105WCr6 | 1.2419 | 56NiCrMoV7

Otai Special provides the Grinding, milling, polishing, turning, drilling, and another machining service as your required tolerances and size.

Processing of 105WCr6 | 1.2419 Steel

1.2419, DIN 105WCr6 Machining, Our production completely according to the 1.2419, DIN 105WCr6 standards to meet the 1.2419, DIN 105WCr6 Machining, can also according to the customer request, to meet the requirements of customers of 1.2419, DIN 105WCr6 Machining.

Packing of 105WCr6 | 1.2419 tool steel

By steel Wire Bundling then put in a container, or as customer require packing.

Welding performance

1.2419, DIN 105WCr6 Welding performance, Our production completely according to the 1.2419, DIN 105WCr6 standards to meet the 1.2419, DIN 105WCr6 Welding performance, can also according to the customer request, to meet the requirements of customers of 1.2419, DIN 105WCr6 Welding performance.