AISI 1045 Carbon Steel G10450 \ Din CK45 W-Nr. 1.1191 JIS S45C Sheet Plate
This steel shows reasonable strength and toughness. AISI 1045 will through harden to 2.5” (63mm) with a tensile strength of 66-120 Ksi (620-850 MPa) . This grade of steel is used for axles, bolts, forged connecting rods, crankshafts, torsion bars, light gears, guide rods etc .
Supply Form of AISI 1045 Carbon Steel G10450 \ Din CK45 W-Nr. 1.1191 JIS S45C
- Round
- sheet
- Plate
- Square
Supply Range of AISI1045 Carbon Steel (CK45)
AISI 1045 Steel Round Bar: diameter 10mm – 400mm
AISI 1045 Steel Plate: thickness 10 –500mm x width 200– 1400mm
AISI 1045 Steel Block: 210mm x 500-810mm
Chemical Composition of AISI1045 (CK45) Material
| ASTM A681 | C | Si | Mn | P | S | Cr | Mo | Ni | Cu | Co |
| 1045/ G10450 | 0.42 ~ 0.50 | 0.17～0.37 | 0.50～0.80 | 0.030 Max | 0.030 Max | ≤0.25 | 0.01 | ≤0.3 | ≤0.25 | / |
| DIN 17350 | C | Si | Mn | P | S | Cr | Mo | Ni | Cu | Co |
| 1.1191/CK45 | 0.42 ~ 0.50 | ≤0.4 | 0.50～0.80 | 0.035 Max | 0.030 Max | ≤0.25 | 0.02 | ≤0.3 | ≤0.25 | / |
| GB/T 1299 | C | Si | Mn | P | S | Cr | Mo | Ni | Cu | Co |
| 45 | 0.42 ~ 0.50 | 0.20～0.45 | 0.50～0.80 | 0.030 Max | 0.030 Max | ≤0.25 | 0.01 | ≤0.3 | ≤0.25 | / |
| JIS G4403 | C | Si | Mn | P | S | Cr | Mo | Ni | Cu | Co |
| S45C | 0.42 ~ 0.48 | 0.15~0.35 | 0.60～0.90 | 0.030 Max | 0.035 Max | ≤0.2 | 0.02 | ≤0.2 | ≤0.3 | / |
AISI1045 (CK45) Material Equivalent and Related Speciations
| USA | German | Japan | China | ISO |
| ASTM A681 | DIN 17350 | JIS G4403 | GB/T 1299 | ISO 4957 |
| 1045 | CK45 | S45C | 45 | C45E4 |
AISI1045 (CK45) Material Mechanical Properties
Hardness, Rockwell C (Water quenched on 820-870°C, 5 minutes): 201~269HB .
Hardness, Rockwell C (Water quenched on 820-870°C, 5 minutes): 201~269HB .
Hardness, Rockwell C(Water quenched on 820-870°C, 5 minutes): 201~269HB .
Forged of AISI1045 (CK45) metal material
At first, Pre-Heating to 552℃，Then heat to forged temperature. Next, Soak at 820-870 °C , ensure heat thorough. Then start forged, the forged temperature no low than 560℃. After forging, cool slowly .
Heat Treatment of AISI 1045 (CK45)
- AISI1045 (CK45) Annealing
Full annealing of small C1045 forgings is carried out from 1450-1600ºF (790-870ºC)
followed by furnace cooling at 50ºF (28ºC) per hour, to 1200ºF (650ºC) soaking and air cooling.
- AISI 1045 (CK45) Hardening
Hardening of this grade is carried out from an austenitizing temperature of 1475-1550ºF (800-845ºC) and oil or water quenching.
Flame and induction hardening may be carried out by heating quickly to the desired case depth and quenching in water or oil. This should be followed by a tempering treatment at 300-400ºF (150-200ºC) to reduce stresses in the case without affecting its hardness. A surface hardness of Rc 58 may be obtained by this treatment.
- Quenching of AISI 1045 (CK45) material
Quenching temperature / ℃ | salt bath furnace: 870
Quenching temperature / ℃ | controlled atmosphere furnace: 870
The heat preservation time/min: 5 ~ 15
Quenching medium: Water cooling
- Tempering Of AISI1045 (CK45)
Tempering temperature / ℃ : 552
After tempering hardness HRC or higher: 201-269HB .
Application of AISI 1045 (CK45)
Suitable for manufacturing various strong cutting tools with wear-resistant, resistant to impact. Advanced punching die, screw die, the toughness and complicated shape of the punch, etc. Roll cutting tool industry: scraper, serrated knife, iron knives, drill bits, etc.
Forging industry: forging die.
Screw industry: heading forming mould, such as teeth, punch
Quality Assured of AISI 1045 (CK45)
Quality assured by ISO 9001:2008 quality management system. Whatsmore, Our all AISI1045 (CK45) all had by SEP 1921-84 ultrasonic inspection (UT Test). Quality Grade: E/e, D/d, C/c.
If you have any AISI1045 (CK45) inquiry and question for Price, Application, hot treatment, Please don’t hesitate to contact us.
Email: Jack@otaisteel.com
Tel: +86-769- 23190193
Fax: +86-769-88705839
More details, please take a look at our website: www.otaisteel.com